MakeItFrom.com
Menu (ESC)

ASTM B617 Coin Silver vs. Solder Alloy 113

Both ASTM B617 coin silver and solder alloy 113 are otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ASTM B617 coin silver and the bottom bar is solder alloy 113.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 75
32
Elongation at Break, % 1.1 to 22
32
Poisson's Ratio 0.37
0.4
Shear Modulus, GPa 28
11
Tensile Strength: Ultimate (UTS), MPa 290 to 520
39

Thermal Properties

Latent Heat of Fusion, J/g 120
40
Melting Completion (Liquidus), °C 870
230
Melting Onset (Solidus), °C 780
180
Specific Heat Capacity, J/kg-K 250
170
Thermal Expansion, µm/m-K 19
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 83
10
Electrical Conductivity: Equal Weight (Specific), % IACS 72
9.8

Otherwise Unclassified Properties

Density, g/cm3 10
9.5

Common Calculations

Stiffness to Weight: Axial, points 4.1
1.8
Stiffness to Weight: Bending, points 14
11
Strength to Weight: Axial, points 7.7 to 14
1.1
Strength to Weight: Bending, points 9.3 to 14
2.7
Thermal Shock Resistance, points 14 to 25
3.4

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0 to 0.050
0 to 0.0050
Copper (Cu), % 9.0 to 10.4
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.050
0 to 0.020
Lead (Pb), % 0 to 0.030
53.4 to 55.5
Nickel (Ni), % 0 to 0.010
0 to 0.010
Phosphorus (P), % 0 to 0.020
0
Silver (Ag), % 89.6 to 91
0 to 0.1
Tin (Sn), % 0
44.5 to 45.5
Zinc (Zn), % 0 to 0.060
0 to 0.0010
Residuals, % 0 to 0.060
0