ASTM B628 Ag-Cu vs. Grade 704C Zirconium
Both ASTM B628 Ag-Cu and grade 704C zirconium are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is grade 704C zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 97 |
| Elongation at Break, % | 1.1 to 17 | |
| 11 |
| Poisson's Ratio | 0.36 | |
| 0.34 |
| Shear Modulus, GPa | 31 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 760 | |
| 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 280 | |
| 270 |
| Thermal Expansion, µm/m-K | 19 | |
| 5.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 6.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.6 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 14 | |
| 23 |
| Strength to Weight: Axial, points | 9.5 to 21 | |
| 20 |
| Strength to Weight: Bending, points | 11 to 18 | |
| 20 |
| Thermal Shock Resistance, points | 16 to 34 | |
| 58 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 26.6 to 29 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.010 |
| Silver (Ag), % | 71 to 73 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.0 to 2.0 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 92.9 to 99 |
| Residuals, % | 0 to 0.21 | |
| 0 |