ASTM B628 Ag-Cu vs. Nickel Beryllium 360
ASTM B628 Ag-Cu belongs to the otherwise unclassified metals classification, while nickel beryllium 360 belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is nickel beryllium 360.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 200 |
| Elongation at Break, % | 1.1 to 17 | |
| 1.0 to 30 |
| Poisson's Ratio | 0.36 | |
| 0.3 |
| Shear Modulus, GPa | 31 | |
| 77 |
| Shear Strength, MPa | 210 to 430 | |
| 510 to 1100 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 760 | |
| 780 to 1860 |
Thermal Properties
| Melting Completion (Liquidus), °C | 780 | |
| 1330 |
| Melting Onset (Solidus), °C | 780 | |
| 1200 |
| Specific Heat Capacity, J/kg-K | 280 | |
| 460 |
| Thermal Expansion, µm/m-K | 19 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 | |
| 5.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 75 | |
| 5.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 9.5 to 21 | |
| 26 to 62 |
| Strength to Weight: Bending, points | 11 to 18 | |
| 23 to 41 |
| Thermal Shock Resistance, points | 16 to 34 | |
| 19 to 46 |