ASTM B628 Ag-Cu vs. K94200 Alloy
ASTM B628 Ag-Cu belongs to the otherwise unclassified metals classification, while K94200 alloy belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is K94200 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 140 |
| Elongation at Break, % | 1.1 to 17 | |
| 5.0 to 32 |
| Poisson's Ratio | 0.36 | |
| 0.34 |
| Shear Modulus, GPa | 31 | |
| 54 |
| Shear Strength, MPa | 210 to 430 | |
| 330 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 760 | |
| 500 to 710 |
Thermal Properties
| Melting Onset (Solidus), °C | 780 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 280 | |
| 500 |
| Thermal Expansion, µm/m-K | 19 | |
| 5.0 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 | |
| 2.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 75 | |
| 3.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.6 | |
| 9.8 |
| Stiffness to Weight: Bending, points | 14 | |
| 21 |
| Strength to Weight: Axial, points | 9.5 to 21 | |
| 17 to 24 |
| Strength to Weight: Bending, points | 11 to 18 | |
| 17 to 22 |
| Thermal Shock Resistance, points | 16 to 34 | |
| 49 to 70 |