MakeItFrom.com
Menu (ESC)

ASTM B628 Ag-Cu vs. N06025 Nickel

ASTM B628 Ag-Cu belongs to the otherwise unclassified metals classification, while N06025 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is N06025 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
200
Elongation at Break, % 1.1 to 17
32
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 31
76
Shear Strength, MPa 210 to 430
500
Tensile Strength: Ultimate (UTS), MPa 350 to 760
760

Thermal Properties

Latent Heat of Fusion, J/g 140
320
Melting Completion (Liquidus), °C 780
1350
Melting Onset (Solidus), °C 780
1300
Specific Heat Capacity, J/kg-K 280
480
Thermal Expansion, µm/m-K 19
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 84
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 75
1.6

Otherwise Unclassified Properties

Density, g/cm3 10
8.2

Common Calculations

Stiffness to Weight: Axial, points 4.6
13
Stiffness to Weight: Bending, points 14
24
Strength to Weight: Axial, points 9.5 to 21
26
Strength to Weight: Bending, points 11 to 18
22
Thermal Shock Resistance, points 16 to 34
21

Alloy Composition

Aluminum (Al), % 0 to 0.0050
1.8 to 2.4
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0.15 to 0.25
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 26.6 to 29
0 to 0.1
Iron (Fe), % 0 to 0.050
8.0 to 11
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0
0 to 0.15
Nickel (Ni), % 0 to 0.010
59.2 to 65.9
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 71 to 73
0
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0.1 to 0.2
Yttrium (Y), % 0
0.050 to 0.12
Zinc (Zn), % 0 to 0.060
0.010 to 0.1
Residuals, % 0 to 0.21
0