ASTM B628 Ag-Cu vs. R30021 Cobalt

ASTM B628 Ag-Cu belongs to the otherwise unclassified metals classification, while R30021 cobalt belongs to the cobalt alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is R30021 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
220
Elongation at Break, % 1.1 to 17
9.0
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 31
86
Tensile Strength: Ultimate (UTS), MPa 350 to 760
700

Thermal Properties

Latent Heat of Fusion, J/g 140
330
Melting Completion (Liquidus), °C 780
1350
Melting Onset (Solidus), °C 780
1190
Specific Heat Capacity, J/kg-K 280
450
Thermal Expansion, µm/m-K 19
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 84
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 75
2.1

Otherwise Unclassified Properties

Density, g/cm3 10
8.4

Common Calculations

Stiffness to Weight: Axial, points 4.6
15
Stiffness to Weight: Bending, points 14
24
Strength to Weight: Axial, points 9.5 to 21
23
Strength to Weight: Bending, points 11 to 18
21
Thermal Shock Resistance, points 16 to 34
21

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0.2 to 0.35
Chromium (Cr), % 0
26 to 29
Cobalt (Co), % 0
61.7 to 67.3
Copper (Cu), % 26.6 to 29
0
Iron (Fe), % 0 to 0.050
0 to 3.0
Lead (Pb), % 0 to 0.030
0
Molybdenum (Mo), % 0
4.5 to 6.0
Nickel (Ni), % 0 to 0.010
2.0 to 3.0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0
0 to 1.5
Silver (Ag), % 71 to 73
0
Zinc (Zn), % 0 to 0.060
0
Residuals, % 0 to 0.21
0