ASTM B631 Class C vs. R60802 Alloy
Both ASTM B631 class C and R60802 alloy are otherwise unclassified metals. There are 11 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is ASTM B631 class C and the bottom bar is R60802 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 180 to 190 | |
98 |
Poisson's Ratio | 0.32 | |
0.34 |
Shear Modulus, GPa | 66 to 71 | |
36 |
Thermal Properties
Latent Heat of Fusion, J/g | 140 to 150 | |
250 |
Specific Heat Capacity, J/kg-K | 180 | |
270 |
Thermal Conductivity, W/m-K | 450 to 490 | |
22 |
Thermal Expansion, µm/m-K | 14 | |
6.0 |
Otherwise Unclassified Properties
Density, g/cm3 | 13 to 14 | |
6.5 |
Common Calculations
Stiffness to Weight: Axial, points | 7.4 to 7.6 | |
8.3 |
Stiffness to Weight: Bending, points | 14 | |
23 |
Thermal Diffusivity, mm2/s | 180 to 200 | |
12 |