ASTM B685 Alloy vs. EN 1.0455 Cast Steel

ASTM B685 alloy belongs to the otherwise unclassified metals classification, while EN 1.0455 cast steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is ASTM B685 alloy and the bottom bar is EN 1.0455 cast steel.

ASTM B685 Palladium-Copper Electrical Contact Alloy EN 1.0455 (GS240) Cast Non-Alloy Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.37
Poisson's Ratio		0.29

Shear Modulus, GPa		43
Shear Modulus, GPa		73

Tensile Strength: Ultimate (UTS), MPa		660 to 1060
Tensile Strength: Ultimate (UTS), MPa		530

Thermal Properties

Latent Heat of Fusion, J/g		180
Latent Heat of Fusion, J/g		250

Melting Completion (Liquidus), °C		1230
Melting Completion (Liquidus), °C		1460

Melting Onset (Solidus), °C		1200
Melting Onset (Solidus), °C		1420

Specific Heat Capacity, J/kg-K		300
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		5.0
Electrical Conductivity: Equal Volume, % IACS		7.1

Electrical Conductivity: Equal Weight (Specific), % IACS		4.1
Electrical Conductivity: Equal Weight (Specific), % IACS		8.1

Otherwise Unclassified Properties

Density, g/cm³		11
Density, g/cm³		7.8

Common Calculations

Stiffness to Weight: Axial, points		6.1
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		15
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		17 to 27
Strength to Weight: Axial, points		19

Strength to Weight: Bending, points		16 to 21
Strength to Weight: Bending, points		18

Thermal Shock Resistance, points		28 to 46
Thermal Shock Resistance, points		17

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0 to 0.23

Copper (Cu), %		39.5 to 40.5
Copper (Cu), %		0

Iron (Fe), %		0 to 0.050
Iron (Fe), %		97.9 to 100

Lead (Pb), %		0 to 0.030
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.2

Palladium (Pd), %		59 to 60.5
Palladium (Pd), %		0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0
Silicon (Si), %		0 to 0.6

Silver (Ag), %		0 to 0.1
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.025

Zinc (Zn), %		0 to 0.060
Zinc (Zn), %		0

Residuals, %		0 to 0.2
Residuals, %		0