ASTM B685 Alloy vs. SAE-AISI T6 Steel
ASTM B685 alloy belongs to the otherwise unclassified metals classification, while SAE-AISI T6 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ASTM B685 alloy and the bottom bar is SAE-AISI T6 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 210 |
| Poisson's Ratio | 0.37 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 1060 | |
| 880 to 2150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 250 |
| Melting Completion (Liquidus), °C | 1230 | |
| 1830 |
| Melting Onset (Solidus), °C | 1200 | |
| 1770 |
| Specific Heat Capacity, J/kg-K | 300 | |
| 400 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 9.5 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.1 | |
| 12 |
| Stiffness to Weight: Bending, points | 15 | |
| 21 |
| Strength to Weight: Axial, points | 17 to 27 | |
| 26 to 63 |
| Strength to Weight: Bending, points | 16 to 21 | |
| 21 to 39 |
| Thermal Shock Resistance, points | 28 to 46 | |
| 26 to 64 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.75 to 0.85 |
| Chromium (Cr), % | 0 | |
| 4.0 to 4.8 |
| Cobalt (Co), % | 0 | |
| 11 to 13 |
| Copper (Cu), % | 39.5 to 40.5 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.050 | |
| 55.9 to 63.5 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.2 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 0.4 to 1.0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Palladium (Pd), % | 59 to 60.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.2 to 0.4 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 18.5 to 21 |
| Vanadium (V), % | 0 | |
| 1.5 to 2.1 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |