ASTM B685 Alloy vs. C70600 Copper-nickel

ASTM B685 alloy belongs to the otherwise unclassified metals classification, while C70600 copper-nickel belongs to the copper alloys. They have 40% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is ASTM B685 alloy and the bottom bar is C70600 copper-nickel.

ASTM B685 Palladium-Copper Electrical Contact Alloy UNS C70600 (CW352H) Copper-Nickel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		120

Poisson's Ratio		0.37
Poisson's Ratio		0.34

Shear Modulus, GPa		43
Shear Modulus, GPa		46

Tensile Strength: Ultimate (UTS), MPa		660 to 1060
Tensile Strength: Ultimate (UTS), MPa		290 to 570

Thermal Properties

Latent Heat of Fusion, J/g		180
Latent Heat of Fusion, J/g		220

Melting Completion (Liquidus), °C		1230
Melting Completion (Liquidus), °C		1150

Melting Onset (Solidus), °C		1200
Melting Onset (Solidus), °C		1100

Specific Heat Capacity, J/kg-K		300
Specific Heat Capacity, J/kg-K		390

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		5.0
Electrical Conductivity: Equal Volume, % IACS		9.8

Electrical Conductivity: Equal Weight (Specific), % IACS		4.1
Electrical Conductivity: Equal Weight (Specific), % IACS		9.9

Otherwise Unclassified Properties

Density, g/cm³		11
Density, g/cm³		8.9

Common Calculations

Stiffness to Weight: Axial, points		6.1
Stiffness to Weight: Axial, points		7.7

Stiffness to Weight: Bending, points		15
Stiffness to Weight: Bending, points		19

Strength to Weight: Axial, points		17 to 27
Strength to Weight: Axial, points		9.1 to 18

Strength to Weight: Bending, points		16 to 21
Strength to Weight: Bending, points		11 to 17

Thermal Shock Resistance, points		28 to 46
Thermal Shock Resistance, points		9.8 to 19

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Copper (Cu), %		39.5 to 40.5
Copper (Cu), %		84.7 to 90

Iron (Fe), %		0 to 0.050
Iron (Fe), %		1.0 to 1.8

Lead (Pb), %		0 to 0.030
Lead (Pb), %		0 to 0.050

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.0

Nickel (Ni), %		0
Nickel (Ni), %		9.0 to 11

Palladium (Pd), %		59 to 60.5
Palladium (Pd), %		0

Silver (Ag), %		0 to 0.1
Silver (Ag), %		0

Zinc (Zn), %		0 to 0.060
Zinc (Zn), %		0 to 1.0

Residuals, %		0
Residuals, %		0 to 0.5