ASTM B780 Alloy vs. 60Cr-40Ni Alloy
Both ASTM B780 alloy and 60Cr-40Ni alloy are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is 60Cr-40Ni alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 220 |
| Poisson's Ratio | 0.36 | |
| 0.25 |
| Shear Modulus, GPa | 30 | |
| 87 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 590 | |
| 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 490 |
| Thermal Expansion, µm/m-K | 18 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.8 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.5 | |
| 16 |
| Stiffness to Weight: Bending, points | 14 | |
| 26 |
| Strength to Weight: Axial, points | 9.1 to 16 | |
| 31 |
| Strength to Weight: Bending, points | 11 to 15 | |
| 26 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.25 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 58 to 62 |
| Copper (Cu), % | 23.5 to 25.7 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 1.0 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0.35 to 0.65 | |
| 34.5 to 42 |
| Nitrogen (N), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Silver (Ag), % | 74 to 76 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 | |
| 0 to 0.5 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 |