ASTM B780 Alloy vs. EN 1.4901 Stainless Steel
ASTM B780 alloy belongs to the otherwise unclassified metals classification, while EN 1.4901 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is EN 1.4901 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 190 |
| Elongation at Break, % | 1.1 to 9.1 | |
| 19 |
| Poisson's Ratio | 0.36 | |
| 0.28 |
| Shear Modulus, GPa | 30 | |
| 76 |
| Shear Strength, MPa | 200 to 340 | |
| 460 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 590 | |
| 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 260 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 470 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 70 to 76 | |
| 8.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 62 to 68 | |
| 9.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.5 | |
| 14 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 9.1 to 16 | |
| 26 |
| Strength to Weight: Bending, points | 11 to 15 | |
| 23 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.020 |
| Boron (B), % | 0 | |
| 0.0010 to 0.0060 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.070 to 0.13 |
| Chromium (Cr), % | 0 | |
| 8.5 to 9.5 |
| Copper (Cu), % | 23.5 to 25.7 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 85.8 to 89.1 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 0.35 to 0.65 | |
| 0 to 0.4 |
| Niobium (Nb), % | 0 | |
| 0.040 to 0.090 |
| Nitrogen (N), % | 0 | |
| 0.030 to 0.070 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Silver (Ag), % | 74 to 76 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 1.5 to 2.0 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.25 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.010 |