ASTM B780 Alloy vs. SAE-AISI H14 Steel
ASTM B780 alloy belongs to the otherwise unclassified metals classification, while SAE-AISI H14 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is SAE-AISI H14 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 190 |
| Poisson's Ratio | 0.36 | |
| 0.29 |
| Shear Modulus, GPa | 30 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 590 | |
| 710 to 2030 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 460 |
| Thermal Expansion, µm/m-K | 18 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 70 to 76 | |
| 9.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 62 to 68 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 9.1 to 16 | |
| 24 to 69 |
| Strength to Weight: Bending, points | 11 to 15 | |
| 22 to 44 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 24 to 68 |
Alloy Composition
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.35 to 0.45 |
| Chromium (Cr), % | 0 | |
| 4.8 to 5.5 |
| Copper (Cu), % | 23.5 to 25.7 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.050 | |
| 86.5 to 89.9 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.2 to 0.5 |
| Nickel (Ni), % | 0.35 to 0.65 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.8 to 1.2 |
| Silver (Ag), % | 74 to 76 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 4.0 to 5.3 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 |