ASTM B780 Alloy vs. C65500 Bronze

ASTM B780 alloy belongs to the otherwise unclassified metals classification, while C65500 bronze belongs to the copper alloys. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is C65500 bronze.

ASTM B780 Silver-Copper-Nickel Electrical Contact Alloy UNS C65500 (CW116C) Silicon Bronze

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		83
Elastic (Young's, Tensile) Modulus, GPa		120

Elongation at Break, %		1.1 to 9.1
Elongation at Break, %		4.0 to 70

Poisson's Ratio		0.36
Poisson's Ratio		0.34

Shear Modulus, GPa		30
Shear Modulus, GPa		43

Shear Strength, MPa		200 to 340
Shear Strength, MPa		260 to 440

Tensile Strength: Ultimate (UTS), MPa		330 to 590
Tensile Strength: Ultimate (UTS), MPa		360 to 760

Thermal Properties

Latent Heat of Fusion, J/g		140
Latent Heat of Fusion, J/g		260

Specific Heat Capacity, J/kg-K		270
Specific Heat Capacity, J/kg-K		400

Thermal Expansion, µm/m-K		18
Thermal Expansion, µm/m-K		18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		70 to 76
Electrical Conductivity: Equal Volume, % IACS		7.0

Electrical Conductivity: Equal Weight (Specific), % IACS		62 to 68
Electrical Conductivity: Equal Weight (Specific), % IACS		7.3

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		8.6

Common Calculations

Stiffness to Weight: Axial, points		4.5
Stiffness to Weight: Axial, points		7.5

Stiffness to Weight: Bending, points		14
Stiffness to Weight: Bending, points		19

Strength to Weight: Axial, points		9.1 to 16
Strength to Weight: Axial, points		12 to 24

Strength to Weight: Bending, points		11 to 15
Strength to Weight: Bending, points		13 to 21

Thermal Shock Resistance, points		16 to 29
Thermal Shock Resistance, points		12 to 26

Alloy Composition

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Copper (Cu), %		23.5 to 25.7
Copper (Cu), %		91.5 to 96.7

Iron (Fe), %		0 to 0.050
Iron (Fe), %		0 to 0.8

Lead (Pb), %		0 to 0.030
Lead (Pb), %		0 to 0.050

Manganese (Mn), %		0
Manganese (Mn), %		0.5 to 1.3

Nickel (Ni), %		0.35 to 0.65
Nickel (Ni), %		0 to 0.6

Silicon (Si), %		0
Silicon (Si), %		2.8 to 3.8

Silver (Ag), %		74 to 76
Silver (Ag), %		0

Zinc (Zn), %		0 to 0.060
Zinc (Zn), %		0 to 1.5

Residuals, %		0
Residuals, %		0 to 0.5