ASTM B817 Type II vs. EN 1.3519 Steel
ASTM B817 type II belongs to the titanium alloys classification, while EN 1.3519 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is ASTM B817 type II and the bottom bar is EN 1.3519 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 900 to 960 | |
| 620 to 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 350 | |
| 430 |
| Melting Completion (Liquidus), °C | 1580 | |
| 1440 |
| Melting Onset (Solidus), °C | 1530 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 480 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 2.6 |
| Density, g/cm3 | 4.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 40 | |
| 1.5 |
| Embodied Energy, MJ/kg | 650 | |
| 21 |
| Embodied Water, L/kg | 220 | |
| 55 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 34 | |
| 25 |
| Strength to Weight: Axial, points | 55 to 58 | |
| 22 to 26 |
| Strength to Weight: Bending, points | 45 to 47 | |
| 21 to 23 |
| Thermal Shock Resistance, points | 62 to 66 | |
| 18 to 22 |
Alloy Composition
| Aluminum (Al), % | 5.0 to 6.0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.1 | |
| 0.93 to 1.1 |
| Chlorine (Cl), % | 0 to 0.2 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 1.4 to 1.7 |
| Copper (Cu), % | 0.35 to 1.0 | |
| 0 to 0.3 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0.35 to 1.0 | |
| 95.4 to 96.8 |
| Manganese (Mn), % | 0 | |
| 1.4 to 1.7 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nitrogen (N), % | 0 to 0.040 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 to 0.0015 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.1 | |
| 0.45 to 0.75 |
| Sodium (Na), % | 0 to 0.2 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 1.5 to 2.5 | |
| 0 |
| Titanium (Ti), % | 82.1 to 87.8 | |
| 0 |
| Vanadium (V), % | 5.0 to 6.0 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |