ASTM B817 Type II vs. N07041 Nickel
ASTM B817 type II belongs to the titanium alloys classification, while N07041 nickel belongs to the nickel alloys. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is ASTM B817 type II and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 220 |
| Elongation at Break, % | 3.0 to 13 | |
| 14 |
| Fatigue Strength, MPa | 390 to 530 | |
| 540 |
| Tensile Strength: Ultimate (UTS), MPa | 900 to 960 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 780 to 900 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1530 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 450 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.6 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 to 120 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2890 to 3890 | |
| 2510 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 34 | |
| 25 |
| Strength to Weight: Axial, points | 55 to 58 | |
| 47 |
| Strength to Weight: Bending, points | 45 to 47 | |
| 34 |
| Thermal Shock Resistance, points | 62 to 66 | |
| 38 |