ASTM F15 Fe-Ni-Co vs. EN 1.4959 Stainless Steel
Both ASTM F15 Fe-Ni-Co and EN 1.4959 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM F15 Fe-Ni-Co and the bottom bar is EN 1.4959 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 880 | |
| 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 300 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1400 |
| Melting Onset (Solidus), °C | 1450 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 480 |
| Thermal Conductivity, W/m-K | 17 | |
| 12 |
| Thermal Expansion, µm/m-K | 6.0 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.7 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.0 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 31 |
| Density, g/cm3 | 8.3 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 5.2 | |
| 5.4 |
| Embodied Energy, MJ/kg | 71 | |
| 76 |
| Embodied Water, L/kg | 190 | |
| 200 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 29 | |
| 22 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 20 |
| Thermal Diffusivity, mm2/s | 4.5 | |
| 3.2 |
| Thermal Shock Resistance, points | 32 to 55 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.1 | |
| 0.25 to 0.65 |
| Carbon (C), % | 0 to 0.040 | |
| 0.050 to 0.1 |
| Chromium (Cr), % | 0 to 0.2 | |
| 19 to 22 |
| Cobalt (Co), % | 16 to 18 | |
| 0 to 0.5 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.5 |
| Iron (Fe), % | 50.3 to 56 | |
| 39.4 to 50.5 |
| Magnesium (Mg), % | 0 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 to 0.2 | |
| 0 |
| Nickel (Ni), % | 28 to 30 | |
| 30 to 34 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0.25 to 0.65 |
| Zirconium (Zr), % | 0 to 0.1 | |
| 0 |