ASTM F15 Fe-Ni-Co vs. K93600 Alloy
Both ASTM F15 Fe-Ni-Co and K93600 alloy are iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is ASTM F15 Fe-Ni-Co and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 880 | |
| 480 to 810 |
Thermal Properties
| Curie Temperature, °C | 430 | |
| 250 |
| Melting Onset (Solidus), °C | 1450 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 520 |
| Thermal Conductivity, W/m-K | 17 | |
| 13 |
| Thermal Expansion, µm/m-K | 6.0 | |
| 7.3 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.7 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.0 | |
| 2.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 8.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 23 | |
| 21 |
| Strength to Weight: Axial, points | 17 to 29 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 17 to 24 |
| Thermal Diffusivity, mm2/s | 4.5 | |
| 3.1 |
| Thermal Shock Resistance, points | 32 to 55 | |
| 34 to 57 |