ASTM F15 Fe-Ni-Co vs. R04295 Alloy
ASTM F15 Fe-Ni-Co belongs to the iron alloys classification, while R04295 alloy belongs to the otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is ASTM F15 Fe-Ni-Co and the bottom bar is R04295 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Poisson's Ratio | 0.3 | |
| 0.38 |
| Shear Modulus, GPa | 73 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 880 | |
| 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 300 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 260 |
| Thermal Expansion, µm/m-K | 6.0 | |
| 7.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 9.0 |
| Embodied Water, L/kg | 190 | |
| 950 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 6.3 |
| Stiffness to Weight: Bending, points | 23 | |
| 17 |
| Strength to Weight: Axial, points | 17 to 29 | |
| 13 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 14 |
| Thermal Shock Resistance, points | 32 to 55 | |
| 40 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.1 | |
| 0 |
| Carbon (C), % | 0 to 0.040 | |
| 0 to 0.015 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0 |
| Cobalt (Co), % | 16 to 18 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 9.0 to 11 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 50.3 to 56 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.2 | |
| 0 |
| Nickel (Ni), % | 28 to 30 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 85.9 to 90.3 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 |
| Tantalum (Ta), % | 0 | |
| 0 to 0.5 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0.7 to 1.3 |
| Tungsten (W), % | 0 | |
| 0 to 0.5 |
| Zirconium (Zr), % | 0 to 0.1 | |
| 0 to 0.7 |