ASTM Grade HC Steel vs. EN 1.0303 Steel
Both ASTM grade HC steel and EN 1.0303 steel are iron alloys. They have 68% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is ASTM grade HC steel and the bottom bar is EN 1.0303 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 6.0 | |
| 12 to 25 |
| Fatigue Strength, MPa | 96 | |
| 150 to 230 |
| Poisson's Ratio | 0.27 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 290 to 410 |
| Tensile Strength: Yield (Proof), MPa | 200 | |
| 200 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 400 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1470 |
| Melting Onset (Solidus), °C | 1370 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 470 |
| Thermal Conductivity, W/m-K | 17 | |
| 53 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 7.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 1.8 |
| Density, g/cm3 | 7.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 40 | |
| 18 |
| Embodied Water, L/kg | 170 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 | |
| 30 to 94 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 95 | |
| 110 to 270 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 26 | |
| 24 |
| Strength to Weight: Axial, points | 16 | |
| 10 to 15 |
| Strength to Weight: Bending, points | 16 | |
| 12 to 16 |
| Thermal Diffusivity, mm2/s | 4.5 | |
| 14 |
| Thermal Shock Resistance, points | 14 | |
| 9.2 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0 to 0.5 | |
| 0.020 to 0.060 |
| Chromium (Cr), % | 26 to 30 | |
| 0 |
| Iron (Fe), % | 61.9 to 74 | |
| 99.335 to 99.71 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.25 to 0.4 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 0 to 4.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 2.0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.025 |