ASTM Grade HG10 MNN Steel vs. EN 1.4962 Stainless Steel

Both ASTM grade HG10 MNN steel and EN 1.4962 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HG10 MNN steel and the bottom bar is EN 1.4962 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
190 to 210
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 23
22 to 34
Fatigue Strength, MPa 170
210 to 330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 590
630 to 690
Tensile Strength: Yield (Proof), MPa 250
260 to 490

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 500
510
Maximum Temperature: Mechanical, °C 990
910
Melting Completion (Liquidus), °C 1420
1480
Melting Onset (Solidus), °C 1370
1440
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 21
23
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 4.0
4.1
Embodied Energy, MJ/kg 58
59
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 25
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
140 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 160
170 to 610
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
21 to 24
Strength to Weight: Bending, points 20
20 to 21
Thermal Diffusivity, mm2/s 3.9
3.7
Thermal Shock Resistance, points 13
14 to 16

Alloy Composition

Boron (B), % 0
0.0015 to 0.0060
Carbon (C), % 0.070 to 0.11
0.070 to 0.15
Chromium (Cr), % 18.5 to 20.5
15.5 to 17.5
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 57.9 to 66.5
62.1 to 69
Manganese (Mn), % 3.0 to 5.0
0 to 1.5
Molybdenum (Mo), % 0.25 to 0.45
0
Nickel (Ni), % 11.5 to 13.5
12.5 to 14.5
Niobium (Nb), % 0.2 to 1.0
0
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 0.7
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.4 to 0.7
Tungsten (W), % 0
2.5 to 3.0