ASTM Grade HG10 MNN Steel vs. SAE-AISI 1005 Steel

Both ASTM grade HG10 MNN steel and SAE-AISI 1005 steel are iron alloys. They have 62% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HG10 MNN steel and the bottom bar is SAE-AISI 1005 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
95
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 23
23
Fatigue Strength, MPa 170
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 590
330
Tensile Strength: Yield (Proof), MPa 250
260

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 990
400
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1370
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
53
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 21
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.0
1.4
Embodied Energy, MJ/kg 58
18
Embodied Water, L/kg 160
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
70
Resilience: Unit (Modulus of Resilience), kJ/m3 160
180
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
12
Strength to Weight: Bending, points 20
13
Thermal Diffusivity, mm2/s 3.9
14
Thermal Shock Resistance, points 13
10

Alloy Composition

Carbon (C), % 0.070 to 0.11
0 to 0.060
Chromium (Cr), % 18.5 to 20.5
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 57.9 to 66.5
99.5 to 100
Manganese (Mn), % 3.0 to 5.0
0 to 0.35
Molybdenum (Mo), % 0.25 to 0.45
0
Nickel (Ni), % 11.5 to 13.5
0
Niobium (Nb), % 0.2 to 1.0
0
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 0.7
0
Sulfur (S), % 0 to 0.030
0 to 0.050