ASTM Grade HG10 MNN Steel vs. SAE-AISI A6 Steel

Both ASTM grade HG10 MNN steel and SAE-AISI A6 steel are iron alloys. They have 66% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HG10 MNN steel and the bottom bar is SAE-AISI A6 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 590
750 to 1990

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
41
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 21
3.7
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
1.8
Embodied Energy, MJ/kg 58
24
Embodied Water, L/kg 160
57

Common Calculations

PREN (Pitting Resistance) 25
4.8
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
27 to 71
Strength to Weight: Bending, points 20
23 to 45
Thermal Diffusivity, mm2/s 3.9
11
Thermal Shock Resistance, points 13
25 to 65

Alloy Composition

Carbon (C), % 0.070 to 0.11
0.65 to 0.75
Chromium (Cr), % 18.5 to 20.5
0.9 to 1.2
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 57.9 to 66.5
93 to 95.8
Manganese (Mn), % 3.0 to 5.0
1.8 to 2.5
Molybdenum (Mo), % 0.25 to 0.45
0.9 to 1.4
Nickel (Ni), % 11.5 to 13.5
0 to 0.3
Niobium (Nb), % 0.2 to 1.0
0
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 0.7
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030