ASTM Grade HL Steel vs. AWS E219

Both ASTM grade HL steel and AWS E219 are iron alloys. They have 76% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HL steel and the bottom bar is AWS E219.

ASTM Grade HL (29Cr-20Ni, N08604) Cast Stainless Steel AWS E219 (W32310) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		11
Elongation at Break, %		17

Poisson's Ratio		0.27
Poisson's Ratio		0.28

Shear Modulus, GPa		80
Shear Modulus, GPa		78

Tensile Strength: Ultimate (UTS), MPa		500
Tensile Strength: Ultimate (UTS), MPa		690

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		290

Melting Completion (Liquidus), °C		1390
Melting Completion (Liquidus), °C		1400

Melting Onset (Solidus), °C		1340
Melting Onset (Solidus), °C		1360

Specific Heat Capacity, J/kg-K		490
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		15

Otherwise Unclassified Properties

Base Metal Price, % relative		27
Base Metal Price, % relative		15

Density, g/cm³		7.8
Density, g/cm³		7.7

Embodied Carbon, kg CO₂/kg material		4.5
Embodied Carbon, kg CO₂/kg material		3.1

Embodied Energy, MJ/kg		65
Embodied Energy, MJ/kg		44

Embodied Water, L/kg		210
Embodied Water, L/kg		160

Common Calculations

PREN (Pitting Resistance)		31
PREN (Pitting Resistance)		25

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		25

Strength to Weight: Bending, points		18
Strength to Weight: Bending, points		23

Thermal Shock Resistance, points		11
Thermal Shock Resistance, points		17

Alloy Composition

Carbon (C), %		0.2 to 0.6
Carbon (C), %		0 to 0.060

Chromium (Cr), %		28 to 32
Chromium (Cr), %		19 to 21.5

Copper (Cu), %		0
Copper (Cu), %		0 to 0.75

Iron (Fe), %		40.8 to 53.8
Iron (Fe), %		58.6 to 67.4

Manganese (Mn), %		0 to 2.0
Manganese (Mn), %		8.0 to 10

Molybdenum (Mo), %		0 to 0.5
Molybdenum (Mo), %		0 to 0.75

Nickel (Ni), %		18 to 22
Nickel (Ni), %		5.5 to 7.0

Nitrogen (N), %		0
Nitrogen (N), %		0.1 to 0.3

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 2.0
Silicon (Si), %		0 to 1.0

Sulfur (S), %		0 to 0.040
Sulfur (S), %		0 to 0.030