ASTM Grade HN Steel vs. AWS E320

Both ASTM grade HN steel and AWS E320 are iron alloys. They have 84% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HN steel and the bottom bar is AWS E320.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.0
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 500
620

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Melting Completion (Liquidus), °C 1400
1410
Melting Onset (Solidus), °C 1350
1360
Specific Heat Capacity, J/kg-K 480
460
Thermal Expansion, µm/m-K 16
14

Otherwise Unclassified Properties

Base Metal Price, % relative 26
38
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 4.6
6.5
Embodied Energy, MJ/kg 66
91
Embodied Water, L/kg 180
220

Common Calculations

PREN (Pitting Resistance) 22
28
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 18
20
Thermal Shock Resistance, points 11
16

Alloy Composition

Carbon (C), % 0.2 to 0.5
0 to 0.070
Chromium (Cr), % 19 to 23
19 to 21
Copper (Cu), % 0
3.0 to 4.0
Iron (Fe), % 44.9 to 57.8
31.8 to 43.5
Manganese (Mn), % 0 to 2.0
0.5 to 2.5
Molybdenum (Mo), % 0 to 0.5
2.0 to 3.0
Nickel (Ni), % 23 to 27
32 to 36
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
0 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.030