ASTM Grade HN Steel vs. SAE-AISI 1211 Steel

Both ASTM grade HN steel and SAE-AISI 1211 steel are iron alloys. They have 52% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HN steel and the bottom bar is SAE-AISI 1211 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
140 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 9.0
11 to 29
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 500
430 to 580

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1080
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 13
52
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 26
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.6
1.4
Embodied Energy, MJ/kg 66
18
Embodied Water, L/kg 180
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
15 to 21
Strength to Weight: Bending, points 18
16 to 20
Thermal Diffusivity, mm2/s 3.5
14
Thermal Shock Resistance, points 11
14 to 18

Alloy Composition

Carbon (C), % 0.2 to 0.5
0 to 0.13
Chromium (Cr), % 19 to 23
0
Iron (Fe), % 44.9 to 57.8
98.7 to 99.23
Manganese (Mn), % 0 to 2.0
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 23 to 27
0
Phosphorus (P), % 0 to 0.040
0.070 to 0.12
Silicon (Si), % 0 to 2.0
0
Sulfur (S), % 0 to 0.040
0.1 to 0.15