ASTM Grade HN Steel vs. SAE-AISI A8 Steel

Both ASTM grade HN steel and SAE-AISI A8 steel are iron alloys. They have 58% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HN steel and the bottom bar is SAE-AISI A8 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
74
Tensile Strength: Ultimate (UTS), MPa 500
700 to 1920

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Melting Completion (Liquidus), °C 1400
1480
Melting Onset (Solidus), °C 1350
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 13
37
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 26
8.5
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.6
2.3
Embodied Energy, MJ/kg 66
31
Embodied Water, L/kg 180
73

Common Calculations

PREN (Pitting Resistance) 22
12
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
25 to 68
Strength to Weight: Bending, points 18
22 to 44
Thermal Diffusivity, mm2/s 3.5
9.9
Thermal Shock Resistance, points 11
22 to 62

Alloy Composition

Carbon (C), % 0.2 to 0.5
0.5 to 0.6
Chromium (Cr), % 19 to 23
4.8 to 5.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 44.9 to 57.8
88.5 to 91.9
Manganese (Mn), % 0 to 2.0
0 to 0.5
Molybdenum (Mo), % 0 to 0.5
1.2 to 1.7
Nickel (Ni), % 23 to 27
0 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 2.0
0.75 to 1.1
Sulfur (S), % 0 to 0.040
0 to 0.030
Tungsten (W), % 0
1.0 to 1.5