ASTM Grade HN Steel vs. C77100 Nickel Silver
ASTM grade HN steel belongs to the iron alloys classification, while C77100 nickel silver belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is ASTM grade HN steel and the bottom bar is C77100 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 77 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 500 | |
| 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 1080 | |
| 150 |
| Melting Completion (Liquidus), °C | 1400 | |
| 990 |
| Melting Onset (Solidus), °C | 1350 | |
| 950 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 13 | |
| 40 |
| Thermal Expansion, µm/m-K | 16 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 27 |
| Density, g/cm3 | 7.9 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 3.5 |
| Embodied Energy, MJ/kg | 66 | |
| 56 |
| Embodied Water, L/kg | 180 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 17 | |
| 21 |
| Strength to Weight: Bending, points | 18 | |
| 20 |
| Thermal Diffusivity, mm2/s | 3.5 | |
| 13 |
| Thermal Shock Resistance, points | 11 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0.2 to 0.5 | |
| 0 |
| Chromium (Cr), % | 19 to 23 | |
| 0 |
| Copper (Cu), % | 0 | |
| 52 to 56 |
| Iron (Fe), % | 44.9 to 57.8 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.030 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 0.9 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 23 to 27 | |
| 9.0 to 12 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 2.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 30.6 to 39 |
| Residuals, % | 0 | |
| 0 to 0.5 |