ASTM Grade HP Steel vs. ASTM A369 Grade FP22
Both ASTM grade HP steel and ASTM A369 grade FP22 are iron alloys. They have a modest 39% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ASTM grade HP steel and the bottom bar is ASTM A369 grade FP22.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 140 | |
140 |
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
190 |
Elongation at Break, % | 5.1 | |
20 |
Fatigue Strength, MPa | 130 | |
160 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 78 | |
74 |
Tensile Strength: Ultimate (UTS), MPa | 490 | |
470 |
Tensile Strength: Yield (Proof), MPa | 260 | |
240 |
Thermal Properties
Latent Heat of Fusion, J/g | 320 | |
260 |
Maximum Temperature: Mechanical, °C | 1100 | |
460 |
Melting Completion (Liquidus), °C | 1370 | |
1470 |
Melting Onset (Solidus), °C | 1330 | |
1430 |
Specific Heat Capacity, J/kg-K | 480 | |
470 |
Thermal Conductivity, W/m-K | 12 | |
39 |
Thermal Expansion, µm/m-K | 16 | |
13 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 34 | |
3.8 |
Density, g/cm3 | 7.9 | |
7.9 |
Embodied Carbon, kg CO2/kg material | 5.8 | |
1.7 |
Embodied Energy, MJ/kg | 82 | |
23 |
Embodied Water, L/kg | 220 | |
58 |
Common Calculations
PREN (Pitting Resistance) | 27 | |
5.5 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 | |
80 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
150 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 17 | |
17 |
Strength to Weight: Bending, points | 17 | |
17 |
Thermal Diffusivity, mm2/s | 3.2 | |
11 |
Thermal Shock Resistance, points | 11 | |
14 |
Alloy Composition
Carbon (C), % | 0.35 to 0.75 | |
0.050 to 0.15 |
Chromium (Cr), % | 24 to 28 | |
1.9 to 2.6 |
Iron (Fe), % | 29.2 to 42.7 | |
95 to 96.9 |
Manganese (Mn), % | 0 to 2.0 | |
0.3 to 0.6 |
Molybdenum (Mo), % | 0 to 0.5 | |
0.87 to 1.1 |
Nickel (Ni), % | 33 to 37 | |
0 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.025 |
Silicon (Si), % | 0 to 2.5 | |
0 to 0.5 |
Sulfur (S), % | 0 to 0.040 | |
0 to 0.025 |