ASTM Grade HP Steel vs. EN 1.5636 Steel

Both ASTM grade HP steel and EN 1.5636 steel are iron alloys. They have a modest 40% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HP steel and the bottom bar is EN 1.5636 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 5.1
27
Fatigue Strength, MPa 130
230
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 490
560
Tensile Strength: Yield (Proof), MPa 260
310

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1370
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
52
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 34
3.6
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 5.8
1.7
Embodied Energy, MJ/kg 82
23
Embodied Water, L/kg 220
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21
130
Resilience: Unit (Modulus of Resilience), kJ/m3 170
260
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 3.2
14
Thermal Shock Resistance, points 11
16

Alloy Composition

Carbon (C), % 0.35 to 0.75
0.060 to 0.12
Chromium (Cr), % 24 to 28
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 29.2 to 42.7
94.6 to 97.4
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 0 to 0.5
0 to 0.2
Nickel (Ni), % 33 to 37
2.0 to 3.0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 2.5
0 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.015
Vanadium (V), % 0
0 to 0.050