ASTM Grade HP Steel vs. SAE-AISI H23 Steel

Both ASTM grade HP steel and SAE-AISI H23 steel are iron alloys. They have 49% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HP steel and the bottom bar is SAE-AISI H23 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 490
760 to 1550

Thermal Properties

Latent Heat of Fusion, J/g 320
260
Melting Completion (Liquidus), °C 1370
1680
Melting Onset (Solidus), °C 1330
1630
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 12
20
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 34
34
Density, g/cm3 7.9
8.7
Embodied Carbon, kg CO2/kg material 5.8
6.9
Embodied Energy, MJ/kg 82
110
Embodied Water, L/kg 220
120

Common Calculations

PREN (Pitting Resistance) 27
32
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 17
24 to 49
Strength to Weight: Bending, points 17
21 to 34
Thermal Diffusivity, mm2/s 3.2
5.2
Thermal Shock Resistance, points 11
23 to 47

Alloy Composition

Carbon (C), % 0.35 to 0.75
0.25 to 0.35
Chromium (Cr), % 24 to 28
11 to 12.8
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 29.2 to 42.7
71.3 to 76.7
Manganese (Mn), % 0 to 2.0
0.15 to 0.4
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 33 to 37
0 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 2.5
0.15 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.030
Tungsten (W), % 0
11 to 12.8
Vanadium (V), % 0
0.75 to 1.3