ASTM Grade HT Steel vs. AWS ENiCrMo-10

ASTM grade HT steel belongs to the iron alloys classification, while AWS ENiCrMo-10 belongs to the nickel alloys. They have 57% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HT steel and the bottom bar is AWS ENiCrMo-10.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 4.6
28
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
84
Tensile Strength: Ultimate (UTS), MPa 500
710

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Melting Completion (Liquidus), °C 1390
1550
Melting Onset (Solidus), °C 1340
1490
Specific Heat Capacity, J/kg-K 480
420
Thermal Conductivity, W/m-K 12
10
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
70
Density, g/cm3 8.0
8.9
Embodied Carbon, kg CO2/kg material 5.4
12
Embodied Energy, MJ/kg 76
160
Embodied Water, L/kg 190
300

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 18
22
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 3.2
2.7
Thermal Shock Resistance, points 12
19

Alloy Composition

Carbon (C), % 0.35 to 0.75
0 to 0.020
Chromium (Cr), % 15 to 19
20 to 22.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 38.2 to 51.7
2.0 to 6.0
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
12.5 to 14.5
Nickel (Ni), % 33 to 37
48.4 to 63
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 2.5
0 to 0.2
Sulfur (S), % 0 to 0.040
0 to 0.015
Tungsten (W), % 0
2.5 to 3.5
Vanadium (V), % 0
0 to 0.35
Residuals, % 0
0 to 0.5