ASTM Grade HT Steel vs. EN 1.0451 Steel

Both ASTM grade HT steel and EN 1.0451 steel are iron alloys. They have 46% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HT steel and the bottom bar is EN 1.0451 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
120
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 4.6
27
Fatigue Strength, MPa 130
180
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 500
420
Tensile Strength: Yield (Proof), MPa 270
240

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1010
400
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
49
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.1
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
1.5
Embodied Energy, MJ/kg 76
19
Embodied Water, L/kg 190
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19
98
Resilience: Unit (Modulus of Resilience), kJ/m3 180
150
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
15
Strength to Weight: Bending, points 18
16
Thermal Diffusivity, mm2/s 3.2
13
Thermal Shock Resistance, points 12
13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0.35 to 0.75
0 to 0.15
Chromium (Cr), % 15 to 19
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 38.2 to 51.7
97.2 to 99.58
Manganese (Mn), % 0 to 2.0
0.4 to 1.2
Molybdenum (Mo), % 0 to 0.5
0 to 0.080
Nickel (Ni), % 33 to 37
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 2.5
0 to 0.35
Sulfur (S), % 0 to 0.040
0 to 0.010
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020