ASTM Grade LC2 Steel vs. AISI 309Cb Stainless Steel

Both ASTM grade LC2 steel and AISI 309Cb stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM grade LC2 steel and the bottom bar is AISI 309Cb stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 27
39
Fatigue Strength, MPa 230
200
Poisson's Ratio 0.29
0.28
Reduction in Area, % 40
46
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 570
580
Tensile Strength: Yield (Proof), MPa 310
230

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 410
1090
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 3.4
23
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.6
4.1
Embodied Energy, MJ/kg 22
59
Embodied Water, L/kg 50
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
180
Resilience: Unit (Modulus of Resilience), kJ/m3 260
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
20
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 17
13

Alloy Composition

Carbon (C), % 0 to 0.25
0 to 0.080
Chromium (Cr), % 0
22 to 24
Iron (Fe), % 95.3 to 97.5
56 to 66
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Nickel (Ni), % 2.0 to 3.0
12 to 16
Niobium (Nb), % 0
0 to 1.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 0.6
0 to 0.75
Sulfur (S), % 0 to 0.045
0 to 0.030