ASTM Grade LC3 Steel vs. ASTM A148 Cast Steel
Both ASTM grade LC3 steel and ASTM A148 cast steel are iron alloys.
For each property being compared, the top bar is ASTM grade LC3 steel and the bottom bar is ASTM A148 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 | |
| 190 to 390 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 27 | |
| 5.7 to 25 |
| Fatigue Strength, MPa | 230 | |
| 280 to 670 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 40 | |
| 13 to 45 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 630 to 1300 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 390 to 1160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 400 to 430 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 52 | |
| 37 to 47 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.6 | |
| 7.3 to 7.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 8.3 to 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.0 | |
| 2.3 to 3.3 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 1.5 to 1.7 |
| Embodied Energy, MJ/kg | 23 | |
| 20 to 22 |
| Embodied Water, L/kg | 52 | |
| 48 to 53 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 71 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 400 to 3570 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 20 | |
| 22 to 46 |
| Strength to Weight: Bending, points | 19 | |
| 21 to 34 |
| Thermal Diffusivity, mm2/s | 14 | |
| 9.9 to 13 |
| Thermal Shock Resistance, points | 17 | |
| 18 to 38 |