ASTM Grade LC4 Steel vs. EN 1.3541 Stainless Steel

Both ASTM grade LC4 steel and EN 1.3541 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM grade LC4 steel and the bottom bar is EN 1.3541 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 570
710

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 410
770
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
30
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 4.6
7.0
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.8
1.9
Embodied Energy, MJ/kg 24
27
Embodied Water, L/kg 54
100

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
26
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 13
8.1
Thermal Shock Resistance, points 17
26

Alloy Composition

Carbon (C), % 0 to 0.15
0.43 to 0.5
Chromium (Cr), % 0
12.5 to 14.5
Iron (Fe), % 93.4 to 95.5
83.4 to 87.5
Manganese (Mn), % 0.5 to 0.8
0 to 1.0
Nickel (Ni), % 4.0 to 5.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.030