ASTM Grade LC9 Steel vs. AWS E33-31

Both ASTM grade LC9 steel and AWS E33-31 are iron alloys. They have 40% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is ASTM grade LC9 steel and the bottom bar is AWS E33-31.

ASTM Grade LC9 (J31300) Cast Nickel Steel AWS E33-31 (W33310) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		210

Elongation at Break, %		22
Elongation at Break, %		29

Poisson's Ratio		0.29
Poisson's Ratio		0.27

Shear Modulus, GPa		73
Shear Modulus, GPa		81

Tensile Strength: Ultimate (UTS), MPa		660
Tensile Strength: Ultimate (UTS), MPa		810

Thermal Properties

Latent Heat of Fusion, J/g		260
Latent Heat of Fusion, J/g		320

Melting Completion (Liquidus), °C		1450
Melting Completion (Liquidus), °C		1380

Melting Onset (Solidus), °C		1410
Melting Onset (Solidus), °C		1330

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		8.0
Base Metal Price, % relative		36

Density, g/cm³		7.9
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		2.3
Embodied Carbon, kg CO₂/kg material		6.0

Embodied Energy, MJ/kg		31
Embodied Energy, MJ/kg		86

Embodied Water, L/kg		65
Embodied Water, L/kg		260

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		23
Strength to Weight: Axial, points		28

Strength to Weight: Bending, points		21
Strength to Weight: Bending, points		24

Thermal Shock Resistance, points		20
Thermal Shock Resistance, points		19

Alloy Composition

Carbon (C), %		0 to 0.13
Carbon (C), %		0 to 0.030

Chromium (Cr), %		0 to 0.5
Chromium (Cr), %		31 to 35

Copper (Cu), %		0 to 0.3
Copper (Cu), %		0.4 to 0.8

Iron (Fe), %		87.4 to 91.5
Iron (Fe), %		24.7 to 34.8

Manganese (Mn), %		0 to 0.9
Manganese (Mn), %		2.5 to 4.0

Molybdenum (Mo), %		0 to 0.2
Molybdenum (Mo), %		1.0 to 2.0

Nickel (Ni), %		8.5 to 10
Nickel (Ni), %		30 to 32

Nitrogen (N), %		0
Nitrogen (N), %		0.3 to 0.5

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.020

Silicon (Si), %		0 to 0.45
Silicon (Si), %		0 to 0.9

Sulfur (S), %		0 to 0.045
Sulfur (S), %		0 to 0.010

Vanadium (V), %		0 to 0.030
Vanadium (V), %		0