ASTM Grade LC9 Steel vs. C33200 Brass
ASTM grade LC9 steel belongs to the iron alloys classification, while C33200 brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is ASTM grade LC9 steel and the bottom bar is C33200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Elongation at Break, % | 22 | |
| 7.0 to 60 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 73 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 320 to 520 |
| Tensile Strength: Yield (Proof), MPa | 590 | |
| 110 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 130 |
| Melting Completion (Liquidus), °C | 1450 | |
| 930 |
| Melting Onset (Solidus), °C | 1410 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Expansion, µm/m-K | 13 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.9 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 28 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 24 |
| Density, g/cm3 | 7.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 2.6 |
| Embodied Energy, MJ/kg | 31 | |
| 44 |
| Embodied Water, L/kg | 65 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
| 35 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 920 | |
| 60 to 960 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 23 | |
| 11 to 17 |
| Strength to Weight: Bending, points | 21 | |
| 13 to 17 |
| Thermal Shock Resistance, points | 20 | |
| 11 to 17 |
Alloy Composition
| Carbon (C), % | 0 to 0.13 | |
| 0 |
| Chromium (Cr), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 65 to 68 |
| Iron (Fe), % | 87.4 to 91.5 | |
| 0 to 0.070 |
| Lead (Pb), % | 0 | |
| 1.5 to 2.5 |
| Manganese (Mn), % | 0 to 0.9 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.2 | |
| 0 |
| Nickel (Ni), % | 8.5 to 10 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 0.45 | |
| 0 |
| Sulfur (S), % | 0 to 0.045 | |
| 0 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 29 to 33.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |