ASTM grade LCC steel belongs to the iron alloys classification, while 86.5-silver 13.5-cadmium-oxide belongs to the otherwise unclassified metals. There are 7 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is ASTM grade LCC steel and the bottom bar is 86.5-silver 13.5-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.8 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 72 to 85 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 64 to 76 |
| Elongation at Break, % | 25 | |
| 3.4 to 16 |
| Strength to Weight: Axial, points | 20 | |
| 7.6 to 11 |
| Strength to Weight: Bending, points | 20 | |
| 9.3 to 12 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 280 to 410 |