AWS BAg-1 vs. EN 1.4417 Stainless Steel

AWS BAg-1 belongs to the otherwise unclassified metals classification, while EN 1.4417 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-1 and the bottom bar is EN 1.4417 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 75
200
Poisson's Ratio 0.33
0.27
Shear Modulus, GPa 28
81
Tensile Strength: Ultimate (UTS), MPa 170
730

Thermal Properties

Latent Heat of Fusion, J/g 110
300
Melting Completion (Liquidus), °C 620
1450
Melting Onset (Solidus), °C 610
1410
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 23
13

Otherwise Unclassified Properties

Density, g/cm3 9.2
7.9
Embodied Carbon, kg CO2/kg material 44
4.1
Embodied Energy, MJ/kg 690
57

Common Calculations

Stiffness to Weight: Axial, points 4.6
15
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 5.1
26
Strength to Weight: Bending, points 7.4
23
Thermal Shock Resistance, points 7.0
20

Alloy Composition

Cadmium (Cd), % 23 to 25
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 14 to 16
0 to 1.0
Iron (Fe), % 0
56.7 to 66.9
Manganese (Mn), % 0
0 to 1.5
Molybdenum (Mo), % 0
3.0 to 4.0
Nickel (Ni), % 0
6.0 to 8.5
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 44 to 46
0
Sulfur (S), % 0
0 to 0.020
Tungsten (W), % 0
0 to 1.0
Zinc (Zn), % 14 to 18
0
Residuals, % 0 to 0.15
0