AWS BAg-1 vs. CC383H Copper-nickel

AWS BAg-1 belongs to the otherwise unclassified metals classification, while CC383H copper-nickel belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-1 and the bottom bar is CC383H copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 75
140
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 28
52
Tensile Strength: Ultimate (UTS), MPa 170
490

Thermal Properties

Latent Heat of Fusion, J/g 110
240
Melting Completion (Liquidus), °C 620
1180
Melting Onset (Solidus), °C 610
1130
Specific Heat Capacity, J/kg-K 280
410
Thermal Expansion, µm/m-K 23
15

Otherwise Unclassified Properties

Density, g/cm3 9.2
8.9
Embodied Carbon, kg CO2/kg material 44
5.7
Embodied Energy, MJ/kg 690
83

Common Calculations

Stiffness to Weight: Axial, points 4.6
8.6
Stiffness to Weight: Bending, points 15
19
Strength to Weight: Axial, points 5.1
15
Strength to Weight: Bending, points 7.4
16
Thermal Shock Resistance, points 7.0
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Bismuth (Bi), % 0
0 to 0.010
Boron (B), % 0
0 to 0.010
Cadmium (Cd), % 23 to 25
0 to 0.020
Carbon (C), % 0
0 to 0.030
Copper (Cu), % 14 to 16
64 to 69.1
Iron (Fe), % 0
0.5 to 1.5
Lead (Pb), % 0
0 to 0.010
Magnesium (Mg), % 0
0 to 0.010
Manganese (Mn), % 0
0.6 to 1.2
Nickel (Ni), % 0
29 to 31
Niobium (Nb), % 0
0.5 to 1.0
Phosphorus (P), % 0
0 to 0.010
Selenium (Se), % 0
0 to 0.010
Silicon (Si), % 0
0.3 to 0.7
Silver (Ag), % 44 to 46
0
Sulfur (S), % 0
0 to 0.010
Tellurium (Te), % 0
0 to 0.010
Zinc (Zn), % 14 to 18
0 to 0.5
Residuals, % 0 to 0.15
0