AWS BAg-10 vs. AWS BAu-1
Both AWS BAg-10 and AWS BAu-1 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much.
For each property being compared, the top bar is AWS BAg-10 and the bottom bar is AWS BAu-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 82 | |
| 110 |
| Poisson's Ratio | 0.35 | |
| 0.37 |
| Shear Modulus, GPa | 30 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 140 | |
| 210 |
Thermal Properties
| Brazing Temperature, °C | 740 to 970 | |
| 1020 to 1090 |
| Latent Heat of Fusion, J/g | 130 | |
| 150 |
| Melting Completion (Liquidus), °C | 740 | |
| 1020 |
| Melting Onset (Solidus), °C | 690 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 280 | |
| 290 |
| Thermal Expansion, µm/m-K | 20 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.8 | |
| 13 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.6 | |
| 4.7 |
| Stiffness to Weight: Bending, points | 15 | |
| 12 |
| Strength to Weight: Axial, points | 4.0 | |
| 4.5 |
| Strength to Weight: Bending, points | 6.1 | |
| 6.1 |
| Thermal Shock Resistance, points | 6.2 | |
| 8.5 |
Alloy Composition
| Copper (Cu), % | 19 to 21 | |
| 61.9 to 63 |
| Gold (Au), % | 0 | |
| 37 to 38 |
| Silver (Ag), % | 69 to 71 | |
| 0 |
| Zinc (Zn), % | 8.0 to 12 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |