AWS BAg-10 vs. C61500 Bronze
AWS BAg-10 belongs to the otherwise unclassified metals classification, while C61500 bronze belongs to the copper alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is AWS BAg-10 and the bottom bar is C61500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 82 | |
| 110 |
| Poisson's Ratio | 0.35 | |
| 0.34 |
| Shear Modulus, GPa | 30 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 140 | |
| 480 to 970 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 220 |
| Melting Completion (Liquidus), °C | 740 | |
| 1040 |
| Melting Onset (Solidus), °C | 690 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 280 | |
| 430 |
| Thermal Expansion, µm/m-K | 20 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.8 | |
| 8.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.6 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 15 | |
| 19 |
| Strength to Weight: Axial, points | 4.0 | |
| 16 to 32 |
| Strength to Weight: Bending, points | 6.1 | |
| 16 to 26 |
| Thermal Shock Resistance, points | 6.2 | |
| 17 to 34 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 7.7 to 8.3 |
| Copper (Cu), % | 19 to 21 | |
| 89 to 90.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.015 |
| Nickel (Ni), % | 0 | |
| 1.8 to 2.2 |
| Silver (Ag), % | 69 to 71 | |
| 0 |
| Zinc (Zn), % | 8.0 to 12 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |