AWS BAg-13 vs. AWS BAg-37
Both AWS BAg-13 and AWS BAg-37 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 70% of their average alloy composition in common.
For each property being compared, the top bar is AWS BAg-13 and the bottom bar is AWS BAg-37.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 91 | |
| 94 |
| Poisson's Ratio | 0.35 | |
| 0.32 |
| Shear Modulus, GPa | 34 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 180 |
Thermal Properties
| Brazing Temperature, °C | 860 to 980 | |
| 780 to 890 |
| Latent Heat of Fusion, J/g | 150 | |
| 150 |
| Melting Completion (Liquidus), °C | 860 | |
| 780 |
| Melting Onset (Solidus), °C | 720 | |
| 690 |
| Specific Heat Capacity, J/kg-K | 310 | |
| 350 |
| Thermal Expansion, µm/m-K | 19 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.7 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 52 | |
| 26 |
| Embodied Energy, MJ/kg | 820 | |
| 410 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.2 | |
| 6.1 |
| Stiffness to Weight: Bending, points | 16 | |
| 18 |
| Strength to Weight: Axial, points | 5.2 | |
| 5.9 |
| Strength to Weight: Bending, points | 7.3 | |
| 8.3 |
| Thermal Shock Resistance, points | 7.5 | |
| 6.6 |
Alloy Composition
| Copper (Cu), % | 37.4 to 42.5 | |
| 39 to 41 |
| Nickel (Ni), % | 0.5 to 1.5 | |
| 0 |
| Silver (Ag), % | 53 to 55 | |
| 24 to 26 |
| Tin (Sn), % | 0 | |
| 1.5 to 2.5 |
| Zinc (Zn), % | 4.0 to 6.0 | |
| 31 to 35 |
| Residuals, % | 0 | |
| 0 to 0.15 |