AWS BAg-13 vs. EN 1.6368 Steel

AWS BAg-13 belongs to the otherwise unclassified metals classification, while EN 1.6368 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-13 and the bottom bar is EN 1.6368 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 91
190
Poisson's Ratio 0.35
0.29
Shear Modulus, GPa 34
73
Tensile Strength: Ultimate (UTS), MPa 180
660 to 690

Thermal Properties

Latent Heat of Fusion, J/g 150
250
Melting Completion (Liquidus), °C 860
1460
Melting Onset (Solidus), °C 720
1420
Specific Heat Capacity, J/kg-K 310
470
Thermal Expansion, µm/m-K 19
13

Otherwise Unclassified Properties

Density, g/cm3 9.7
7.9
Embodied Carbon, kg CO2/kg material 52
1.7
Embodied Energy, MJ/kg 820
22

Common Calculations

Stiffness to Weight: Axial, points 5.2
13
Stiffness to Weight: Bending, points 16
24
Strength to Weight: Axial, points 5.2
23 to 24
Strength to Weight: Bending, points 7.3
21 to 22
Thermal Shock Resistance, points 7.5
20

Alloy Composition

Aluminum (Al), % 0
0.015 to 0.040
Carbon (C), % 0
0 to 0.17
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 37.4 to 42.5
0.5 to 0.8
Iron (Fe), % 0
95.1 to 97.2
Manganese (Mn), % 0
0.8 to 1.2
Molybdenum (Mo), % 0
0.25 to 0.5
Nickel (Ni), % 0.5 to 1.5
1.0 to 1.3
Niobium (Nb), % 0
0.015 to 0.045
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0.25 to 0.5
Silver (Ag), % 53 to 55
0
Sulfur (S), % 0
0 to 0.010
Zinc (Zn), % 4.0 to 6.0
0
Residuals, % 0 to 0.15
0