AWS BAg-13a vs. AWS BAg-33
Both AWS BAg-13a and AWS BAg-33 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 55% of their average alloy composition in common.
For each property being compared, the top bar is AWS BAg-13a and the bottom bar is AWS BAg-33.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 92 | |
| 85 |
| Poisson's Ratio | 0.36 | |
| 0.32 |
| Shear Modulus, GPa | 34 | |
| 32 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 170 |
Thermal Properties
| Brazing Temperature, °C | 720 to 980 | |
| 680 to 840 |
| Latent Heat of Fusion, J/g | 160 | |
| 130 |
| Melting Completion (Liquidus), °C | 890 | |
| 680 |
| Melting Onset (Solidus), °C | 770 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 300 | |
| 320 |
| Thermal Expansion, µm/m-K | 19 | |
| 23 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.8 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 54 | |
| 25 |
| Embodied Energy, MJ/kg | 850 | |
| 400 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.2 | |
| 5.5 |
| Stiffness to Weight: Bending, points | 15 | |
| 17 |
| Strength to Weight: Axial, points | 5.1 | |
| 5.5 |
| Strength to Weight: Bending, points | 7.2 | |
| 7.9 |
| Thermal Shock Resistance, points | 7.5 | |
| 6.3 |
Alloy Composition
| Cadmium (Cd), % | 0 | |
| 16.5 to 18.5 |
| Copper (Cu), % | 40.4 to 43.5 | |
| 29 to 31 |
| Nickel (Ni), % | 1.5 to 2.5 | |
| 0 |
| Silver (Ag), % | 55 to 57 | |
| 24 to 26 |
| Zinc (Zn), % | 0 | |
| 26.5 to 28.5 |
| Residuals, % | 0 | |
| 0 to 0.15 |