AWS BAg-13a vs. EN 1.4436 Stainless Steel
AWS BAg-13a belongs to the otherwise unclassified metals classification, while EN 1.4436 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is AWS BAg-13a and the bottom bar is EN 1.4436 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 92 | |
| 200 |
| Poisson's Ratio | 0.36 | |
| 0.28 |
| Shear Modulus, GPa | 34 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 290 |
| Melting Completion (Liquidus), °C | 890 | |
| 1450 |
| Melting Onset (Solidus), °C | 770 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 300 | |
| 470 |
| Thermal Expansion, µm/m-K | 19 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 54 | |
| 3.9 |
| Embodied Energy, MJ/kg | 850 | |
| 54 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 15 | |
| 25 |
| Strength to Weight: Axial, points | 5.1 | |
| 22 |
| Strength to Weight: Bending, points | 7.2 | |
| 20 |
| Thermal Shock Resistance, points | 7.5 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 16.5 to 18.5 |
| Copper (Cu), % | 40.4 to 43.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 62.3 to 70.5 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 2.5 to 3.0 |
| Nickel (Ni), % | 1.5 to 2.5 | |
| 10.5 to 13 |
| Nitrogen (N), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Silver (Ag), % | 55 to 57 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Residuals, % | 0 to 0.15 | |
| 0 |