AWS BAg-13a vs. Nickel 685

AWS BAg-13a belongs to the otherwise unclassified metals classification, while nickel 685 belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-13a and the bottom bar is nickel 685.

AWS BAg-13a (P07560) Filler Metal Nickel Alloy 685 (N07001)

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		92
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.36
Poisson's Ratio		0.29

Shear Modulus, GPa		34
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		180
Tensile Strength: Ultimate (UTS), MPa		1250

Thermal Properties

Latent Heat of Fusion, J/g		160
Latent Heat of Fusion, J/g		320

Melting Completion (Liquidus), °C		890
Melting Completion (Liquidus), °C		1380

Melting Onset (Solidus), °C		770
Melting Onset (Solidus), °C		1330

Specific Heat Capacity, J/kg-K		300
Specific Heat Capacity, J/kg-K		460

Thermal Expansion, µm/m-K		19
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Density, g/cm³		9.8
Density, g/cm³		8.4

Embodied Carbon, kg CO₂/kg material		54
Embodied Carbon, kg CO₂/kg material		10

Embodied Energy, MJ/kg		850
Embodied Energy, MJ/kg		140

Common Calculations

Stiffness to Weight: Axial, points		5.2
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		15
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		5.1
Strength to Weight: Axial, points		42

Strength to Weight: Bending, points		7.2
Strength to Weight: Bending, points		31

Thermal Shock Resistance, points		7.5
Thermal Shock Resistance, points		37

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		1.2 to 1.6

Boron (B), %		0
Boron (B), %		0.0030 to 0.010

Carbon (C), %		0
Carbon (C), %		0.030 to 0.1

Chromium (Cr), %		0
Chromium (Cr), %		18 to 21

Cobalt (Co), %		0
Cobalt (Co), %		12 to 15

Copper (Cu), %		40.4 to 43.5
Copper (Cu), %		0 to 0.5

Iron (Fe), %		0
Iron (Fe), %		0 to 2.0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		3.5 to 5.0

Nickel (Ni), %		1.5 to 2.5
Nickel (Ni), %		49.6 to 62.5

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0
Silicon (Si), %		0 to 0.75

Silver (Ag), %		55 to 57
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Titanium (Ti), %		0
Titanium (Ti), %		2.8 to 3.3

Zinc (Zn), %		0
Zinc (Zn), %		0.020 to 0.12

Residuals, %		0 to 0.15
Residuals, %		0