AWS BAg-18 vs. N06110 Nickel

AWS BAg-18 belongs to the otherwise unclassified metals classification, while N06110 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-18 and the bottom bar is N06110 nickel.

AWS BAg-18 (P07600) Filler Metal UNS N06110 Nickel Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		82
Elastic (Young's, Tensile) Modulus, GPa		210

Poisson's Ratio		0.36
Poisson's Ratio		0.28

Shear Modulus, GPa		30
Shear Modulus, GPa		84

Tensile Strength: Ultimate (UTS), MPa		170
Tensile Strength: Ultimate (UTS), MPa		730

Thermal Properties

Latent Heat of Fusion, J/g		130
Latent Heat of Fusion, J/g		340

Melting Completion (Liquidus), °C		720
Melting Completion (Liquidus), °C		1490

Melting Onset (Solidus), °C		600
Melting Onset (Solidus), °C		1440

Specific Heat Capacity, J/kg-K		280
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		19
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Density, g/cm³		9.7
Density, g/cm³		8.6

Embodied Carbon, kg CO₂/kg material		59
Embodied Carbon, kg CO₂/kg material		11

Embodied Energy, MJ/kg		930
Embodied Energy, MJ/kg		160

Common Calculations

Stiffness to Weight: Axial, points		4.7
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		15
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		4.9
Strength to Weight: Axial, points		23

Strength to Weight: Bending, points		7.0
Strength to Weight: Bending, points		21

Thermal Shock Resistance, points		7.7
Thermal Shock Resistance, points		20

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 1.0

Carbon (C), %		0
Carbon (C), %		0 to 0.15

Chromium (Cr), %		0
Chromium (Cr), %		28 to 33

Copper (Cu), %		28.4 to 31.5
Copper (Cu), %		0 to 0.5

Iron (Fe), %		0
Iron (Fe), %		0 to 1.0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		9.0 to 12

Nickel (Ni), %		0
Nickel (Ni), %		51 to 62

Niobium (Nb), %		0
Niobium (Nb), %		0 to 1.0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.5

Silicon (Si), %		0
Silicon (Si), %		0 to 1.0

Silver (Ag), %		59 to 61
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.015

Tin (Sn), %		9.5 to 10.5
Tin (Sn), %		0

Titanium (Ti), %		0
Titanium (Ti), %		0 to 1.0

Tungsten (W), %		0
Tungsten (W), %		1.0 to 4.0

Residuals, %		0 to 0.15
Residuals, %		0