AWS BAg-1a vs. AWS BAg-2
Both AWS BAg-1a and AWS BAg-2 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 85% of their average alloy composition in common.
For each property being compared, the top bar is AWS BAg-1a and the bottom bar is AWS BAg-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 77 | |
| 82 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 29 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 180 |
Thermal Properties
| Brazing Temperature, °C | 640 to 760 | |
| 700 to 840 |
| Latent Heat of Fusion, J/g | 120 | |
| 130 |
| Melting Completion (Liquidus), °C | 640 | |
| 700 |
| Melting Onset (Solidus), °C | 630 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 280 | |
| 310 |
| Thermal Expansion, µm/m-K | 22 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 48 | |
| 35 |
| Embodied Energy, MJ/kg | 760 | |
| 550 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.6 | |
| 5.1 |
| Stiffness to Weight: Bending, points | 15 | |
| 16 |
| Strength to Weight: Axial, points | 5.4 | |
| 5.6 |
| Strength to Weight: Bending, points | 7.6 | |
| 7.9 |
| Thermal Shock Resistance, points | 7.5 | |
| 7.0 |
Alloy Composition
| Cadmium (Cd), % | 17 to 19 | |
| 17 to 19 |
| Copper (Cu), % | 14.5 to 16.5 | |
| 25 to 27 |
| Silver (Ag), % | 49 to 51 | |
| 34 to 36 |
| Zinc (Zn), % | 14.5 to 18.5 | |
| 19 to 23 |
| Residuals, % | 0 | |
| 0 to 0.15 |